Anaerobic Anaterm-103 is designed for bonding and sealing of flat and smooth cylindrical (landing) compounds.

Clay is different at high speed curing and high tearing strength.

Anaterm-103 is a viscous homogenous liquid capable of long-term stay in the initial state in the presence of oxygen and cure rapidly in a narrow gap between the bonding surfaces to form a strong adhesive bond.

Anaterm-103 does not require an activator to the metal surface.

It is used for bonding of various materials: metal, glass, laminated glass, ceramics and some plastics.

Details before applying the adhesive must be degreased and cleaned of contaminants. After degreasing parts are dried to evaporate the solvent.

Physical and mechanical properties

Indicator Anaterm-103

Appearance Homogeneous liquid from light yellow to brown

Kinematic vyazkost.106 at 20 ° C, m2 / s 900-1400

Tensile strength at break, MPa, at least at 20-25 ° C over 24 hours without activator

at 120 ° C after 0.5 hours

thirty

thirty

Tensile strength at the axial shear 20-30 MPa

Time to reach handling strength at 20-25 ° C, min. 20-25

Ready for use at 20-25 ° C, 5-12 hours

Pot life at 60 ° C, h, not less than 1

Operating temperature range, ° C -60 ... + 150

The maximum gap of 0.2 mm

Note: the material used in the feature that its curing occurs only in a certain clearance on the free surface of the adhesive is not cured (that is not married), and removed using rags.

Precautionary measures:

Keep away from food at temperatures from +5 to + 30 ° C, protected from direct sunlight and dirt ingress into the vial.

After contact with the sealant on the skin, wash it off with soap and water.

The sealant is ready for use, has a long pot life when stored.

It supplied in plastic bottles.