Glue K-300-61 (Клей К-300-61)

Synonyms: Compound K-300-61, glue K-300.

COMPOSITION: is a three-component set consisting of epoxy-organosilane resin, amine hardener and filler (paste-like mass).

COMPOSITION COMPONENTS: resin "Dekalit 6", polyamide L-20, filler.

TRANSPORTATION: possible by any mode of transport in accordance with the rules for the carriage of goods. During transportation is not dangerous.

GUARANTEED SHELF LIFE - 1 year from the date of manufacture.

PACKAGING: Plastic or metal containers (buckets, canisters) of various capacities. Standard shipping rate: 1.7 kg. Non-standard packing is possible in agreement with the consumer.

/The image of the product in the picture may differ from the original./

Glue K-300-61 (Клей К-300-61)

 is intended for hermetic bonding of asbestos and fiberglass, steels, aluminum and titanium alloys, brass, ceramics, foam plastics, graphite, fluoroplast, including those working under mechanical loads and in extreme temperature conditions from -196°C to +300°С (1 minute); at +200°C (1000 hours).

Recommended for use in products of aviation and space technology.

Glue K-300-61 (Клей К-300-61)

- has high adhesion to various kinds of surfaces, incl. glues asbestos and fiberglass, steel, aluminum and titanium alloys, brass, ceramics, foam plastics, graphite, fluoroplast;

- high-strength glue;

- heat-resistant adhesive, operating in a wide temperature range from -196°C to +300°C (1 minute); at +200°C (1000 hours).

Glue K-300-61 (Клей К-300-61)

Name of indicator  Norm
Appearance Pasty homogeneous mass from white to light brown
Pot life at (20+5)ºС, h not less than   1,0
Glue consumption per one layer, g/m2  200-300
Holding time of adhesive joints, h

at a temperature of +15-30°С  

at a temperature of +60+5°С  

at a temperature of +80+5°С 

24

10

 4

Shear strength of adhesive joints made of steel at +20°C, MPa (kgf/cm2)   9 (90)
Peel strength of adhesive joints made of steel, MPa (kgf/cm2)

at a temperature of +20°С  

at a temperature of +300°С  

20 (200)

1 (10)